Anycubic ABS-Like 3.0 resin is a photopolymer resin for LCD and DLP 3D printers that use ultraviolet light with a wavelength of 365–405 nm. It has low volumetric shrinkage and elongation at break of up to 30%, while its impact strength is 130 J/m. Its low viscosity helps reproduce fine details and allows the resin to flow during printing.

The formulation has minimal odor and a low tendency to warp. The resin can be used to print mechanical components, device housings and automotive parts, as well as models subject to stress or further machining.

• Resin type: ABS-Like
• Color: Gray
• Material: Photopolymer resin
• Compatibility: LCD and DLP 3D printers
• Printing wavelength: 365–405 nm
• Viscosity: 280–300 mPa·s at 25 °C
• Density: 1.06–1.09 g/cm³
• Hardness: 83–86 HD
• Tensile strength: 38–45 MPa
• Elongation at break: 25–30%
• Flexural modulus: 50–65 MPa
• Flexural strength: 1500–2000 MPa
• Young's modulus: 1300–1700 MPa
• Izod impact strength: 130 J/m
• Volumetric shrinkage: 3.9–4.9%
• Printing temperature: 20–50 °C
• Recommended ambient temperature during printing: 20–40 °C
• Bottom layer exposure time: 23–40 s
• Normal layer exposure time: 2–3.6 s
• Cleaning agent: 95% IPA
• Washing time: At least 3 minutes
• UV wavelength during curing: 405 nm
• Curing temperature: 18–30 °C
• UV intensity: 25,000–30,000 μW/cm²
• Curing time: 3 minutes
• Weight: 1 kg