Anycubic ABS-Like 3.0 photopolymer resin is designed for LCD and DLP 3D printers that use ultraviolet light with a wavelength of 365–405 nm. It has low volumetric shrinkage and a viscosity of 280–300 mPa·s, helping produce accurate details and a smooth surface. Elongation at break of 25–30% and impact strength of 130 J/m make it suitable for mechanical parts and device housings.

The resin has a low odor and a low tendency to warp. Use 95% IPA to clean printed models.

• Resin type: ABS-Like
• Color: White
• Material: Photopolymer resin
• Compatibility: LCD and DLP 3D printers
• Printing wavelength: 365–405 nm
• Viscosity: 280–300 mPa·s at 25 °C
• Density: 1.06–1.09 g/cm³
• Hardness: 83–86 HD
• Tensile strength: 38–45 MPa
• Elongation at break: 25–30%
• Flexural modulus: 50–65 MPa
• Flexural strength: 1500–2000 MPa
• Young's modulus: 1300–1700 MPa
• Izod impact strength: 130 J/m
• Volumetric shrinkage: 3.9–4.9%
• Printing temperature: 20–50 °C
• Recommended printing ambient temperature: 20–40 °C
• First-layer exposure time: 23–40 s
• Normal-layer exposure time: 2–3.6 s
• Cleaning agent: 95% IPA
• Washing time: At least 3 minutes
• UV wavelength for curing: 405 nm
• Curing temperature: 18–30 °C
• UV irradiance: 25,000–30,000 μW/cm²
• Curing time: 3 minutes
• Weight: 1 kg