PrimaCreator Value UV / DLP Flex Resin is designed for printing detailed, flexible objects with low shrinkage and high impact resistance. It is optimized for 395–405 nm UV light sources and performs well with low-power DLP 3D printers.

Curing time is 4–12 seconds per 0.05 mm layer, depending on the color, while the first layer requires 40–60 seconds. After printing, rinse the object with isopropyl alcohol (IPA) and cure it in a UV chamber for approximately 2–5 minutes, in sunlight for 10–20 minutes, or for up to 60 minutes on a cloudy day.

• Type: UV / DLP Flex Resin
• Color: Transparent
• Capacity: 500 ml
• Compatibility: PrimaCreator 3D printers
• UV wavelength: 395–405 nm
• Shore D hardness: 65–75 D
• Elongation at break: 130%
• Flexural modulus: 1,882–2,385 MPa
• Flexural strength: 40–70 MPa
• Tensile strength: 30–52 MPa
• Tensile modulus: 1,779–2,385 MPa
• Heat deflection temperature: 80 ℃
• Glass transition temperature: 100 ℃
• Thermal expansion: 95*E-6
• Volumetric shrinkage: 3.72–4.24%
• Linear shrinkage: 1.05–1.35%
• Density: 1.05–1.25 g/cm3
• Notched impact strength: 41–48 j/m
• Viscosity: 150–300 MPa·s
• Curing time per layer: 4–12 s for a 0.05 mm layer thickness
• First-layer curing time: 40–60 s